Cold Rolled AISI434 / EN 1.4113 Stainless Steel Sheets & Plate 0.4 - 3.0mm Thickness

Name: Cold Rolled AISI434 EN 14113 Stainless Steel Sheets amp Plate 04 30mm Thickness
Brand: TISCO
Price: 1600 USD

Wholesale Cold Rolled AISI434 / EN 1.4113 Stainless Steel Sheets & Plate 0.4 - 3.0mm Thickness from china suppliers

Brand Name : TISCO

Model Number : AISI434 / EN 1.4113

Certification : ISO

Place of Origin : China

MOQ : 500 kgs

Price : 1600 - 1800USD/Ton

Payment Terms : T/T, Western Union, L/C

Supply Ability : 10 Ton per week

Delivery Time : 5 - 12 days based on the quantity

Packaging Details : standard packing for export

Products : Stainless Steel Sheet

Grade : Stainless Steel AISI434 / EN 1.4113

Standard : ASTM EN JIS GB

Size : 1219*2438mm

Thickness : 0.5 - 3.0mm

Type : cold rolled

Service : cutting, surface treatment

application : auto exhaust pipe

Packing : wooden pallets

Contact Now

Cold Rolled AISI434 / EN 1.4113 Stainless Steel Sheets & Plate 0.4 - 3.0mm Thickness

Products Specification

Products Name	AISI434 Stainless Steel Sheet
Standard	ASTM EN JIS GB BIS
Thickness	0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm 2.0mm 2.5mm 3.0mm
Surface	2B 2D NO.1 or process other surface as request
Standard Size	12192438mm 10002000mm
Service	Slit Cutting, bending , surface treatment
Other Grade	200 Series: 201 202
	300 Series: 301 304 304L 309S 310S 316L 316Ti 317l 321 329 347
	400 Series: 409L 410S 416 420 431 436L 439 441 443 444 446
	Special Grade: 254SMO 904L 2205 2507 253MA Nickel Alloy
MOQ	500 kgs
Packing	Wooden Pallets and waterproof paper

Stainless steels are high-alloy steels. They have high corrosion resistance due to high chromium content of about 4-30%. They are classified in to three types such as ferritic, austenitic, and martensitic steels based on their crystalline structure.

Grade 434 stainless steel contains added molybdenum to increase its corrosion resistance. It is has performance and chemistry similar to that of 430 stainless steel.

Chemical Composition

The following table shows the chemical composition of grade 434 stainless steel.

Grade	C	Si	Mn	P	S	Cr	Mo	Fe
AISI434 / EN 1.4113	0.12	1.00	1.00	0.04	0.03	16.0-18.00	0.8-1.25	Bal

Mechanical Properties

The following table outlines the mechanical properties of annealed grade 434 stainless steel.

Properties	Metric	Imperial
Tensile strength	538 MPa	78000 psi
Yield strength (@ strain 0.200%)	441 MPa	64000 psi
Elastic modulus	200 GPa	29008 ksi
Poisson's ratio	0.27-0.30	0.27-0.30
Elongation at break (in 50 mm)	32%	32%
Hardness, Rockwell B (converted from Brinell hardness)	89	89

Other designations that are equivalent to grade 434 stainless steel include:

DIN 1.4113
AFNOR Z 8 CD 17.01
UNI X 8 CrMo 17
JIS SUS 434
SS 2325
B.S. 434 S 19
ASTM A65i
SAE 51434
SAE J405 (51434)

Machinability

Grade 434 stainless steel can be machined using all standard procedures.

Forming

Blanking, shearing, and deep drawing operations can be successfully performed due to its high ductility.

Welding

Grade 434 stainless steel can be welded using common techniques. After welding, it should be thoroughly cleaned to increase corrosion resistance property.

Forging

Grade 434 stainless steel can be forged at 1094 -1149°C (2000-2100°F) after thorough soaking.

Annealing

Grade 434 stainless steel is annealed by soaking at 788 - 872°C (1450-1600°F) followed by cooling in air.

Hardening

Grade 434 stainless steel does not react to heat treatment.

Cold Rolled AISI434 / EN 1.4113 Stainless Steel Sheets & Plate 0.4 - 3.0mm Thickness